CHENSHI
2000 Metric Ton/Metric Tons per Month
Tianjin/shanghai/Qingdao
1 Metric Ton/Metric Tons
T/T,L/C,Western Union,MoneyGram,Paypal payments for offline orders.
TiO2 content % | 94%min |
Rutile crystal content % | 98.5%min |
Surface treatment | Al2O3, ZrO2 |
Volatile constituents at 105℃ % | 0.6%max |
Residue, 45μm % | 0.01%max |
PH | 6.0-9.0 |
Resistivity, Ω·m | 80 min |
Oil absorption, g/100g | 21.0 max |
CIE L* | 97.5 min |
CIE b* | 1.3 max |
Tinctorial power | 1950 min |
Specific gravity, g/cm3 | 4.1 |
Dispersion, Hegman | 6.5 min |
TiO2 content % | 94%min |
Surface treatment | Al2O3, SiO2,ZrO2 |
Volatile constituents at 105℃ % | 0.5%max |
Residue, 45μm % | 0.01%max |
PH | 6.0-9.0 |
Resistivity, Ω·m | 80 min |
Oil absorption, g/100g | 18 max |
CIE L* | 98.0 min |
CIE b* | 1.0 max |
Specific gravity, g/cm3 | 4.1 |
TiO2 content % | 94%min |
Rutile crystal content % | 98.5%min |
Surface treatment | Al2O3, ZrO2 |
Volatile constituents at 105℃ % | 0.6%max |
Residue, 45μm % | 0.01%max |
PH | 6.0-9.0 |
Resistivity, Ω·m | 80 min |
Oil absorption, g/100g | 21.0 max |
CIE L* | 97.5 min |
CIE b* | 1.3 max |
Tinctorial power | 1950 min |
Specific gravity, g/cm3 | 4.1 |
Dispersion, Hegman | 6.5 min |
TiO2 content % | 94%min |
Surface treatment | Al2O3, SiO2,ZrO2 |
Volatile constituents at 105℃ % | 0.5%max |
Residue, 45μm % | 0.01%max |
PH | 6.0-9.0 |
Resistivity, Ω·m | 80 min |
Oil absorption, g/100g | 18 max |
CIE L* | 98.0 min |
CIE b* | 1.0 max |
Specific gravity, g/cm3 | 4.1 |